Structure, sinterability, chemical stability and conductivity of proton-conducting BaZr0.6M0.2Y0.2O3−δ electrolyte membranes: The effect of the M dopant

Yu Liu, Ran Ran, Moses O. Tade, Zongping Shao
Journal of membrane science 2014 v.467 pp. 100-108
artificial membranes, carbon dioxide, cathodes, cations, ceramics, cerium, fuel cells, hydrogen
BaZr0.8Y0.2O3 (BZY) may be one of the most promising proton conductors for hydrogen separation membranes and proton-conducting solid oxide fuel cells. Doping strategies have been widely applied to improve the sintering activity and conductivity of BZY ceramics. In this study, the phase structure, sinterability, chemical stability and conductivity of BaZr0.6M0.2Y0.2O3−δ (BZMY) compositions with various M cations of Zr⁴⁺, Ce⁴⁺, Pr³⁺, Nd³⁺, Sm³⁺ and Gd³⁺ with different ionic radii were comparatively studied. All the rare-earth dopants could improve the sinterability of BZY. As the ionic radii of the dopants decreased, the oxides are more and more stable in the CO2 atmosphere. EIS results indicated that a greater ionic conductivity was achieved for BZMY with a larger M dopant. Among the various composites, BZNY and BZCY showed favorable protonic conductivity at 600°C in a wet 10% H2–Ar atmosphere, with good sinterability and resistance to CO2 attack. A peak power density of 153mWcm⁻² was achieved at 700°C with a fuel cell that contained BZCY as an electrolyte and BSCF as a cathode.